PBN Boat
1. Product Insturction
Before the compound semiconductor single crystal growth, it is
usually synthesis the compound semiconductor polycrystalline
material first.
PBN Boat is ideal vessel for polycrystalline synthesis.
2. Product Feature
High Purity (99.999%)
No wetting with melt metal
Thermal conductivity controllable, improve the rate of yield
Excellent thermal shock resistance
Easy cleaning and Reusability
Inert, no reaction with acid and alkali
PBN Boat
1. Product Insturction
Before the compound semiconductor single crystal growth, it is
usually synthesis the compound semiconductor polycrystalline
material first.
PBN Boat is ideal vessel for polycrystalline synthesis.
2. Product Feature
High Purity (99.999%)
No wetting with melt metal
Thermal conductivity controllable, improve the rate of yield
Excellent thermal shock resistance
Easy cleaning and Reusability
Inert, no reaction with acid and alkali
PBN Boat
1. Product Insturction
Before the compound semiconductor single crystal growth, it is
usually synthesis the compound semiconductor polycrystalline
material first.
PBN Boat is ideal vessel for polycrystalline synthesis.
2. Product Feature
High Purity (99.999%)
No wetting with melt metal
Thermal conductivity controllable, improve the rate of yield
Excellent thermal shock resistance
Easy cleaning and Reusability
Inert, no reaction with acid and alkali
Specification:
*This form is for typical sizes, other size is customizable.
Parameter of PBN
1. Product Insturction
Before the compound semiconductor single crystal growth, it is
usually synthesis the compound semiconductor polycrystalline
material first.
PBN Boat is ideal vessel for polycrystalline synthesis.
2. Product Feature
High Purity (99.999%)
No wetting with melt metal
Thermal conductivity controllable, improve the rate of yield
Excellent thermal shock resistance
Easy cleaning and Reusability
Inert, no reaction with acid and alkali
PBN Boat
1. Product Insturction
Before the compound semiconductor single crystal growth, it is
usually synthesis the compound semiconductor polycrystalline
material first.
PBN Boat is ideal vessel for polycrystalline synthesis.
2. Product Feature
High Purity (99.999%)
No wetting with melt metal
Thermal conductivity controllable, improve the rate of yield
Excellent thermal shock resistance
Easy cleaning and Reusability
Inert, no reaction with acid and alkali
PBN Boat
1. Product Insturction
Before the compound semiconductor single crystal growth, it is
usually synthesis the compound semiconductor polycrystalline
material first.
PBN Boat is ideal vessel for polycrystalline synthesis.
2. Product Feature
High Purity (99.999%)
No wetting with melt metal
Thermal conductivity controllable, improve the rate of yield
Excellent thermal shock resistance
Easy cleaning and Reusability
Inert, no reaction with acid and alkali
Specification:
Catalog No | Length | Height | Thickness |
BOAT-1" | 2"~15" | 0.5"~1" | 0.035"~0.08" |
BOAT-2" | 6"~20" | 1" | 0.035"~0.08" |
BOAT-3" | 6"~20" | 1.5" | 0.035"~0.08" |
BOAT-4" | 6"~20" | 2" | 0.035"~0.08" |
Parameter of PBN
Properties | Units | Values |
Density | g/cm3 | 1.95-2.20 |
Tensile Strength | MPa | 112 |
Bending Strength | MPa | 173 |
Compression Strength | MPa | 154 |
Young's Modulus | GPa | 18 |
Thermal Conductivity | W/m°C | "a" 60 "c" 2 |
Specific Heat | J/g·ºC | 0.90(RT) |
Resistivity | Ω.cm | 2×1015 |
Dielectric Strength | D.C. volts/mm | 2×1015 |
Dielectric Constant | "c" 3.07 | |
Metal Impurity Content | ppm | <10 |